1) Each profiles surface protected by transparent or logo film, and several profile wrap to be bundle by shrink film.
2) Each profiles interleaf by EPE form, and several profile wrap to be bundle by shrink film.
3) Each profiles surface protect by film or interleaf by EPE form, and several profile roll by paper.
2.Wood pallets packing:
Step 1: Dozens of bundle alu profile put on the wood pallet base, and fixed by strip film.
Step 2: Cover the alu profiles by thick paper and wrap by shrink film.
Step 3: Surrounded the pallet by numbers of wood strip and fixed to be firmed pallet by pvc or iron strip.
Each profile interleaf by EPE form or pack by plastic bag, dozens of alu profile put in carton and seal & strengthen by tape.
|Dimensional deviations info(6063-T5)||Angle deviation:±1.0°|
|Plane clearance: less than 0.37mm|
|Bending degree: less than 0.3mmfrom 300mm|
|Twist degree: less than 1.7mm from 1m profile|
|Cutting angle: less than 2°|
|Mechanical characteristic (6063-T5)||Vickers hardness (HV)≥58|
|Webster hardness (HW)≥8|
|Tensile strength: no less than 160 N/mm²|
|Anodizing characteristic||Average thickness of anodize film: no less than 10 μm|
|Partial thickness of anodize film: no less than 8 μm|
|Anodize sealing quality: no less than 30 mg/dm²|
|Hardness (Pential scratch testing): ≥ 3H|
|CASS test (24h):≥ 9 grade|
|Alkali resistance(24h):no less than 9 grade|
|Wear resistance(sand drop testing): ≥300 g/μm|
|Powder coating characteristic||Coating indentation hardness: ≥ 80|
|Coating thickness: 60 ~ 120 μm|
|Smallest local thickness: > 40 μm|
|adhension (dry、wet、boiling water): 0 grade|
|Wear resistance(sand drop testing): ≥0.8 L/μm|
|Hydrochloric Acid resistance: no blistering and obvious change|
|Solvent resistance: ≥ 3 grade|
|Detergent resistance: no blistering, no loss of film adhension and obvious change|
|Mortar resistance: no loss of film adhension and no visual change in appearance|
|Boiling water resistance: no air bubble、 wrinkle、cracks、falls off and color change on test specimen|